The hardness of electron beam deposited (EBD) titanium carbide films onto Ti substrates was studied. It was found that high temperature of substrate pre-heating results in decreasing hardness of titanium carbide film onto titanium substrate. Even at the substrate pre-heating temperature of about 200°C, the hardness of EBD titanium carbide was found to be lower than that of bulk TiC ceramics.
Hardness of electron beam deposited titanium carbide films on titanium substrate / Ferro, Daniela; Scandurra, Roberto; Latini, Alessandro; J. V., Rau; S. M., Barinov. - In: JOURNAL OF MATERIALS SCIENCE. - ISSN 0022-2461. - 39:1(2004), pp. 329-330. [10.1023/b:jmsc.0000007767.87299.84]
Hardness of electron beam deposited titanium carbide films on titanium substrate
FERRO, DANIELA;SCANDURRA, Roberto;LATINI, ALESSANDRO;
2004
Abstract
The hardness of electron beam deposited (EBD) titanium carbide films onto Ti substrates was studied. It was found that high temperature of substrate pre-heating results in decreasing hardness of titanium carbide film onto titanium substrate. Even at the substrate pre-heating temperature of about 200°C, the hardness of EBD titanium carbide was found to be lower than that of bulk TiC ceramics.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.