Platinum nanoparticles (PtNPs), with diameters of 3-10 nm, were synthesized by water phase reduction, using 3-mercapto-1-propanesulfonate (3MPS) as a hydrophilic capping agent. PtNPs were deposited by a dipcoating technique on titania nanofibers (TiO2NFs), obtained by electrospinning. The investigated properties of the Pt-TiO2 hybrid at room temperature show that this material combines the properties of photoconduction of titania and the photocatalytic activity of the hybrid. To assess the best performance of Pt-TiO2, different measurements were performed at room temperature, comparing hydrogen response under UV of the uncoated TiO2NFs, compared with the Pt-TiO2 system prepared with two different amounts of PtNPs. During the sensing tests toward hydrogen an enhancement of photoconductivity (150%), an increase in response (400%) and an overall improvement of their dynamic behaviour were observed.
Platinum nanoparticles (PtNPs), with diameters of 3-10 nm, were synthesized by water phase reduction, using 3-mercapto-1-propanesulfonate (3MPS) as a hydrophilic capping agent. PtNPs were deposited by a dipcoating technique on titania nanofibers (TiO2NFs), obtained by electrospinning. The investigated properties of the Pt-TiO2 hybrid at room temperature show that this material combines the properties of photoconduction of titania and the photocatalytic activity of the hybrid. To assess the best performance of Pt-TiO2, different measurements were performed at room temperature, comparing hydrogen response under UV of the uncoated TiO2NFs, compared with the Pt-TiO2 system prepared with two different amounts of PtNPs. During the sensing tests toward hydrogen an enhancement of photoconductivity (150%), an increase in response (400%) and an overall improvement of their dynamic behaviour were observed. This journal is © the Partner Organisations 2014.
Platinum nanoparticles on electrospun titania nanofibers as hydrogen sensing materials working at room temperature / Fratoddi, Ilaria; Antonella, Macagnano; Chiara, Battocchio; Emiliano, Zampetti; Venditti, Iole; Russo, Maria Vittoria; Andrea, Bearzotti. - In: NANOSCALE. - ISSN 2040-3364. - 6:15(2014), pp. 9177-9184. [10.1039/c4nr01400f]
Platinum nanoparticles on electrospun titania nanofibers as hydrogen sensing materials working at room temperature
FRATODDI, Ilaria;VENDITTI, Iole;RUSSO, Maria Vittoria;
2014
Abstract
Platinum nanoparticles (PtNPs), with diameters of 3-10 nm, were synthesized by water phase reduction, using 3-mercapto-1-propanesulfonate (3MPS) as a hydrophilic capping agent. PtNPs were deposited by a dipcoating technique on titania nanofibers (TiO2NFs), obtained by electrospinning. The investigated properties of the Pt-TiO2 hybrid at room temperature show that this material combines the properties of photoconduction of titania and the photocatalytic activity of the hybrid. To assess the best performance of Pt-TiO2, different measurements were performed at room temperature, comparing hydrogen response under UV of the uncoated TiO2NFs, compared with the Pt-TiO2 system prepared with two different amounts of PtNPs. During the sensing tests toward hydrogen an enhancement of photoconductivity (150%), an increase in response (400%) and an overall improvement of their dynamic behaviour were observed.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.