We report the preliminary results of the implementation of innovative ceramic thermal barrier coatings (TBC) produced by plasma thermal spraying. The materials used are part of the class of rare earth zirconates, in this case, lanthanum and cerium, characterized by structure and piroclorica fluoritica. Their use would overcome the operational limits imposed by the materials of use corrente.Sono been developed procedures for treatment of the starting materials (La2O3, ZrO2, CeO2), in order to obtain powders suitable for termodeposizione having the desired compositions (La2Zr2O7 , La2 (Zr0.7Ce0.3) 2O7). The various types of powders were then deposited using different sets of parameters, allowing to identify the deposition process more idoneo.Le analysis on coatings obtained showed firstly the goodness of the treatment technique of the powders, and then the deposition process , allowing you to obtain coatings containing the desired phase.
Vengono riportati i risultati preliminari della realizzazione di barriere termiche ceramiche innovative (TBC) realizzate per termospruzzatura plasma. I materiali utilizzati fanno parte della classe degli zirconati di terre rare, in questo caso di lantanio e cerio, caratterizzati da struttura piroclorica e fluoritica. Il loro utilizzo consentirebbe di superare i limiti operativi imposti dai materiali di utilizzo corrente. Sono state messe a punto procedure di trattamento dei materiali di partenza (La2O3, ZrO2, CeO2), al fine di ottenere polveri idonee alla termodeposizione aventi le composizioni desiderate (La2Zr2O7, La2(Zr0.7Ce0.3)2O7). Le varie tipologie di polveri sono state quindi depositate utilizzando diversi set di parametri, permettendo di individuare il processo di deposizione più idoneo. Le analisi sui rivestimenti ottenuti hanno dimostrato in primo luogo la bontà della tecnica di trattamento delle polveri, e quindi del processo di deposizione, consentendo di ottenere rivestimenti contenenti la fase desiderata.
Rivestimenti ceramici di nuova generazione per termodeposizione plasma / Marra, Francesco; M., Tului; R., Pileggi; Pulci, Giovanni; Tirillo', Jacopo; Sarasini, Fabrizio; Bartuli, Cecilia; Valente, Marco; Valente, Teodoro. - (2012), pp. 339-342. (Intervento presentato al convegno XI Convegno AIMAT tenutosi a Gaeta (LT) nel 11-19 Settembre 2012).
Rivestimenti ceramici di nuova generazione per termodeposizione plasma
MARRA, FRANCESCO;PULCI, Giovanni;TIRILLO', Jacopo;SARASINI, Fabrizio;BARTULI, Cecilia;VALENTE, Marco;VALENTE, Teodoro
2012
Abstract
We report the preliminary results of the implementation of innovative ceramic thermal barrier coatings (TBC) produced by plasma thermal spraying. The materials used are part of the class of rare earth zirconates, in this case, lanthanum and cerium, characterized by structure and piroclorica fluoritica. Their use would overcome the operational limits imposed by the materials of use corrente.Sono been developed procedures for treatment of the starting materials (La2O3, ZrO2, CeO2), in order to obtain powders suitable for termodeposizione having the desired compositions (La2Zr2O7 , La2 (Zr0.7Ce0.3) 2O7). The various types of powders were then deposited using different sets of parameters, allowing to identify the deposition process more idoneo.Le analysis on coatings obtained showed firstly the goodness of the treatment technique of the powders, and then the deposition process , allowing you to obtain coatings containing the desired phase.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.