Li cells based on BiF3 cathodes have been tested. In particular, the effect ofcathode formulation and compacting pressure, nature of the solution, temperature,and current density have been evaluated. Through x-ray analysis, cyclicvoltammetry, and coulometric analysis it was possible to ascertain that BiF3is reduced to Bi and then to Li3Bi. During the first reduction process, ternaryphases of the LixBiF3 type are probably formed. Li/BiF3 cells can give practicalenergy densities in excess of 200 W-hr/kg at the rate of 0.5 mA/cm2

Nonaqueous Batteries with BiF3 Cathodes / P., Fiordiponti; Panero, Stefania; G., Pistoia; C., Temperoni. - In: JOURNAL OF THE ELECTROCHEMICAL SOCIETY. - ISSN 0013-4651. - STAMPA. - 125:4(1978), pp. 511-515. [10.1149/1.2131487]

Nonaqueous Batteries with BiF3 Cathodes

PANERO, Stefania;
1978

Abstract

Li cells based on BiF3 cathodes have been tested. In particular, the effect ofcathode formulation and compacting pressure, nature of the solution, temperature,and current density have been evaluated. Through x-ray analysis, cyclicvoltammetry, and coulometric analysis it was possible to ascertain that BiF3is reduced to Bi and then to Li3Bi. During the first reduction process, ternaryphases of the LixBiF3 type are probably formed. Li/BiF3 cells can give practicalenergy densities in excess of 200 W-hr/kg at the rate of 0.5 mA/cm2
1978
01 Pubblicazione su rivista::01a Articolo in rivista
Nonaqueous Batteries with BiF3 Cathodes / P., Fiordiponti; Panero, Stefania; G., Pistoia; C., Temperoni. - In: JOURNAL OF THE ELECTROCHEMICAL SOCIETY. - ISSN 0013-4651. - STAMPA. - 125:4(1978), pp. 511-515. [10.1149/1.2131487]
File allegati a questo prodotto
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11573/475770
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 23
  • ???jsp.display-item.citation.isi??? ND
social impact