Hot dip galvanizing is one of most important processing techniques to protect metallic materials against corrosion in many aggressive environments containing Cl-. In the last years new elements added in the bath have oriented many studies to obtain coatings characterized by different behaviors, optimized to large deformation or better external aspect. In this work an innovative zinc bath containing 0.5% wt of Titanium and 1% wt of Tin was used to generate coatings on rectangular specimens made on ipersandelin steel. Coatings, obtained for dipping times in the bath of 15, 60, 180, 360 and 900s were undergoing to bending tests. Finally metallographic analyses were performed on longitudinal section in order to evaluate intermetallic phases damage. La zincatura a caldo è una delle tecniche di protezione contro la corrosione più utilizzate grazie alle elevate caratteristiche di protezione dei rivestimenti e al basso costo di realizzazione. Negli ultimi anni sono stati sperimentati diversi bagni a base zinco per l’ottenimento di rivestimenti dalla caratteristiche peculiari ottimizzati per i diversi aspetti via via richiesti nelle applicazioni pratiche. In questo lavoro è stato utilizzato un bagno di zinco innovativo contenente lo 0,5% in peso di titanio e l’1% in peso di stagno. I provini zincati sono stati realizzati in acciaio ipersandelin e sottoposti a prove di flessione. I provini piegati sono stati utilizzati per l’analisi metallografica del danno delle fasi intermetalliche.
Scheda prodotto non validato
Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo
Titolo: | Influence of 0.5%Ti and 1%Sn in intermetallic phases damage in Hot Dip Galvanizing Coating Influenza dello 0.5%Ti e 1%Sn sul danneggiamento dei rivestimenti a base zinco | |
Autori: | ||
Data di pubblicazione: | 2012 | |
Handle: | http://hdl.handle.net/11573/438701 | |
ISBN: | 9788895940434 | |
Appartiene alla tipologia: | 04b Atto di convegno in volume |