Nickel-cobalt alloys having settled composition can be produced by electrolysis after optimising process operative conditions. In this work nickel-cobalt coatings on 1050 Al net, obtained by electrodeposition under galvanostatic conditions, were investigated. Ni-Co coatings were electrowon, from an acidic sulphate bath containing 40 g/L Ni and Co in the range 0.1-16 g/L, at 60 degrees C temperature and 300 A/m(2) average current density. The experimental results highlight a linear correlation between bath and deposit Co/Ni ratio, with slope change for Co concentration in the electrolyte higher than 3 g/L. Morphology, structure and electrochemical properties are strictly correlated among themselves and with the composition of the coating. (C) 2011 Elsevier B.V. All rights reserved.
Composition, morphology, structural aspects and electrochemical properties of Ni-Co alloy coatings / Lupi, Carla; Dell'Era, Alessandro; Pasquali, Mauro; P., Imperatori. - In: SURFACE & COATINGS TECHNOLOGY. - ISSN 0257-8972. - STAMPA. - 205:23-24(2011), pp. 5394-5399. [10.1016/j.surfcoat.2011.06.002]
Composition, morphology, structural aspects and electrochemical properties of Ni-Co alloy coatings
LUPI, Carla;DELL'ERA, Alessandro;PASQUALI, Mauro;
2011
Abstract
Nickel-cobalt alloys having settled composition can be produced by electrolysis after optimising process operative conditions. In this work nickel-cobalt coatings on 1050 Al net, obtained by electrodeposition under galvanostatic conditions, were investigated. Ni-Co coatings were electrowon, from an acidic sulphate bath containing 40 g/L Ni and Co in the range 0.1-16 g/L, at 60 degrees C temperature and 300 A/m(2) average current density. The experimental results highlight a linear correlation between bath and deposit Co/Ni ratio, with slope change for Co concentration in the electrolyte higher than 3 g/L. Morphology, structure and electrochemical properties are strictly correlated among themselves and with the composition of the coating. (C) 2011 Elsevier B.V. All rights reserved.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.