The present work was performed with the aim of characterizing various plasma sprayed Cr3C2-NiCr coatings produced by using different processing pressures between 300 and 1200 mbars, in a nitrogen controlled atmosphere CAPS system. X-Ray diffraction was carried out on all coatings by using Bragg-Brentano geometry. The phases identified in the as-supplied powder Cr3C2/Ni-Cr were fcc Ni-Cr and orthorhombic Cr3C2. In contrast to the original powder, the coatings showed evidence of Cr3C2, Ni-Cr and either Cr6.2C3.5N0.3 or Cr3C1.52N0.48 carbo-nitride phases depending on the ratio of C/N in the coating. The presence of Cr7C3 and CrO2 was also identified in the coatings deposited at atmospheric pressure. The volume fraction of carbide plus nitride phase in the coating was always less than the volume fractions of the carbide phase in the original feed stock powder. The volume fraction of carbide plus nitride phase was found to depend quite markedly on the spraying parameters such as pressure, power input, spraying distance and substrate cooling. The results have been presented in terms of spraying efficiency, ξ. The highest value of ξ (86.4%) was obtained for coatings produced at 1200 mbar pressure, a spraying distance of 120 mm, without N2 cooling and the lowest value (25.2%) was found for the coatings deposited at 300 mbar for the same spraying distance but with N2 cooling. The presence of graphitic carbon was detected in all samples especially for specimens where the fraction of carbide plus carbo-nitride phases was the greatest. The influence of spraying parameters such as pressure, power input, spraying distance and substrate cooling on the microstructure was determined. The highest microhardness value of 2296 HV50 was found for the carbide plus carbo-nitride phase contained in the specimens produced at 1200 mbar spraying pressure, 120-mm spraying distance and substrate heating at 600°C. © 2001 Elsevier Science B.V. All rights reserved.
Part I: Characterization of Cr3C2-25% NiCr reactive plasma sprayed coatings produced at different pressures / M. H., Staia; Valente, Teodoro; Bartuli, Cecilia; D. B., Lewis; C. P., Constable. - In: SURFACE & COATINGS TECHNOLOGY. - ISSN 0257-8972. - STAMPA. - 146-147:(2001), pp. 553-562. [10.1016/s0257-8972(01)01437-2]
Part I: Characterization of Cr3C2-25% NiCr reactive plasma sprayed coatings produced at different pressures
VALENTE, Teodoro;BARTULI, Cecilia;
2001
Abstract
The present work was performed with the aim of characterizing various plasma sprayed Cr3C2-NiCr coatings produced by using different processing pressures between 300 and 1200 mbars, in a nitrogen controlled atmosphere CAPS system. X-Ray diffraction was carried out on all coatings by using Bragg-Brentano geometry. The phases identified in the as-supplied powder Cr3C2/Ni-Cr were fcc Ni-Cr and orthorhombic Cr3C2. In contrast to the original powder, the coatings showed evidence of Cr3C2, Ni-Cr and either Cr6.2C3.5N0.3 or Cr3C1.52N0.48 carbo-nitride phases depending on the ratio of C/N in the coating. The presence of Cr7C3 and CrO2 was also identified in the coatings deposited at atmospheric pressure. The volume fraction of carbide plus nitride phase in the coating was always less than the volume fractions of the carbide phase in the original feed stock powder. The volume fraction of carbide plus nitride phase was found to depend quite markedly on the spraying parameters such as pressure, power input, spraying distance and substrate cooling. The results have been presented in terms of spraying efficiency, ξ. The highest value of ξ (86.4%) was obtained for coatings produced at 1200 mbar pressure, a spraying distance of 120 mm, without N2 cooling and the lowest value (25.2%) was found for the coatings deposited at 300 mbar for the same spraying distance but with N2 cooling. The presence of graphitic carbon was detected in all samples especially for specimens where the fraction of carbide plus carbo-nitride phases was the greatest. The influence of spraying parameters such as pressure, power input, spraying distance and substrate cooling on the microstructure was determined. The highest microhardness value of 2296 HV50 was found for the carbide plus carbo-nitride phase contained in the specimens produced at 1200 mbar spraying pressure, 120-mm spraying distance and substrate heating at 600°C. © 2001 Elsevier Science B.V. All rights reserved.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.