Elettrodeposizione pulsata di rivestimenti di rame su fibre ottiche rivestite in poliimmide per applicazioni FBG criogeniche

This work investigates the metallisation of polyimide-coated optical fibres by combining Au sputtering and Cu electrodeposition for potential application to FBG sensors operating under cryogenic conditions. Direct- and pulsed-current regimes were compared, and coating coverage, surface morphology and apparent thickness were evaluated by scanning electron microscopy. Cu covered the visible fibre surface under all the investigated conditions. Pulsed deposition generally produced more uniform surfaces, whereas regimes involving a higher nominal charge resulted in more developed and heterogeneous morphologies. Because the effects of current waveform and supplied charge were not fully decoupled, the results should be regarded as a preliminary screening. They provide a basis for charge-matched experiments and for selecting coatings for subsequent electrical and cryogenic characterisation.

Il lavoro esamina la metallizzazione di fibre ottiche rivestite in poliimmide mediante sputtering di Au ed elettrodeposizione di Cu, in vista dell’impiego su sensori FBG per applicazioni criogeniche. Sono stati confrontati regimi di corrente continua e pulsata, valutando mediante microscopia elettronica a scansione la copertura, la morfologia superficiale e lo spessore apparente dei rivestimenti. In tutte le condizioni esaminate, il Cu ha ricoperto la superficie visibile della fibra. Le deposizioni pulsate hanno generalmente prodotto superfici più uniformi, mentre i regimi caratterizzati da una maggiore carica nominale hanno determinato morfologie più sviluppate ed eterogenee. Poiché gli effetti della forma d’onda e della carica non sono stati completamente disaccoppiati, i risultati costituiscono uno screening preliminare per successive prove a parità di carica e per la selezione dei rivestimenti da sottoporre a caratterizzazione elettrica e criogenica.