Dynamic Mechanical Behavior of Nanosilica-Based Epoxy Composites Under LEO-like UV-C Exposure

The harsh conditions of the space environment necessitate advanced materials capable of withstanding extreme temperature fluctuations and ultraviolet (UV) radiation. While epoxy-based composites are widely utilized in aerospace due to their favorable strength-to-weight ratio, they are prone to degradation, especially under prolonged high-energy UV-C exposure. This study investigated the mechanical and chemical stability of epoxy composites reinforced with nanosilica at 0, 2, 5, and 10 wt% before and after UV-C irradiation. Dynamic mechanical analysis (DMA) revealed that increased nanosilica content enhanced the storage modulus below the glass transition temperature (Tg) but reduced both Tg and the damping factor. Following UV-C exposure, all samples showed a decrease in storage modulus and Tg; however, composites with higher nanosilica content maintained better property retention. Frequency sweeps corroborated these findings, indicating improved instantaneous modulus but accelerated relaxation with increased nanosilica. Fourier-transform infrared (FTIR) spectroscopy of UV-C-exposed samples demonstrated significant oxidation and carboxylic group formation in neat epoxy, contrasting with minimal spectral changes in nanosilica-modified composites, signifying improved chemical resistance. Overall, nanosilica incorporation substantially enhances the thermomechanical and oxidative stability of epoxy composites under simulated space conditions, highlighting their potential for more durable performance in low Earth orbit applications.