Methane cracking is considered a bridge technology between gray and green hydrogen production processes. In this work an experimental study of methane cracking in molten tin is performed. The tests were conducted in a quartz reactor (i.d. = 1.5 cm, L = 20 cm) with capillary injection, varying temperature (950-1070 C-degrees), inlet methane flow rate (30-60 mL.min(-1)) and tin height (0-20 cm). The influence of the residence time in the tin and in the headspace on methane conversion and on carbon morphology was investigated. The conversions obtained in tin and in the empty reactor were measured and compared with results of detailed kinetic simulations (CRECK). Furthermore, an expression of a global kinetic constant for methane conversion in tin was also derived. The highest conversion (65% at Q(0) = 30 mL.min(-1) and t = 1070 C-degrees) is obtained for homogeneous gas phase reaction due to the long residence time (70 s), the presence of tin leads to a sharp decrease of residence time (1 s), obtaining a conversion of 35% at 1070 C-degrees, thus meaning that tin owns a role in the reaction. Carbon characterization (scanning electron microscopy, Raman) reported a change in carbon toward sheet-like structures and an increase of the carbon structural order in the presence of molten tin media.

Methane cracking in molten tin for hydrogen and carbon production—a comparison with homogeneous gas phase process / Busillo, Emmanuel; de Caprariis, Benedetta; Bracciale, Maria Paola; Cosentino, Vittoria; Damizia, Martina; Iaquaniello, Gaetano; Palo, Emma; De Filippis, Paolo. - In: FRONTIERS OF CHEMICAL SCIENCE AND ENGINEERING. - ISSN 2095-0179. - 18:7(2024). [10.1007/s11705-024-2437-x]

Methane cracking in molten tin for hydrogen and carbon production—a comparison with homogeneous gas phase process

Busillo, Emmanuel
Primo
;
de Caprariis, Benedetta
;
Bracciale, Maria Paola;Damizia, Martina;De Filippis, Paolo
Ultimo
2024

Abstract

Methane cracking is considered a bridge technology between gray and green hydrogen production processes. In this work an experimental study of methane cracking in molten tin is performed. The tests were conducted in a quartz reactor (i.d. = 1.5 cm, L = 20 cm) with capillary injection, varying temperature (950-1070 C-degrees), inlet methane flow rate (30-60 mL.min(-1)) and tin height (0-20 cm). The influence of the residence time in the tin and in the headspace on methane conversion and on carbon morphology was investigated. The conversions obtained in tin and in the empty reactor were measured and compared with results of detailed kinetic simulations (CRECK). Furthermore, an expression of a global kinetic constant for methane conversion in tin was also derived. The highest conversion (65% at Q(0) = 30 mL.min(-1) and t = 1070 C-degrees) is obtained for homogeneous gas phase reaction due to the long residence time (70 s), the presence of tin leads to a sharp decrease of residence time (1 s), obtaining a conversion of 35% at 1070 C-degrees, thus meaning that tin owns a role in the reaction. Carbon characterization (scanning electron microscopy, Raman) reported a change in carbon toward sheet-like structures and an increase of the carbon structural order in the presence of molten tin media.
2024
methane cracking; molten media; H-2 production; carbon morphology
01 Pubblicazione su rivista::01a Articolo in rivista
Methane cracking in molten tin for hydrogen and carbon production—a comparison with homogeneous gas phase process / Busillo, Emmanuel; de Caprariis, Benedetta; Bracciale, Maria Paola; Cosentino, Vittoria; Damizia, Martina; Iaquaniello, Gaetano; Palo, Emma; De Filippis, Paolo. - In: FRONTIERS OF CHEMICAL SCIENCE AND ENGINEERING. - ISSN 2095-0179. - 18:7(2024). [10.1007/s11705-024-2437-x]
File allegati a questo prodotto
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11573/1724770
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 2
  • ???jsp.display-item.citation.isi??? 2
social impact