Comparison of coronal discoloration induced by White MTA and CEM Cement

Coronal discoloration of endodontically treated teeth is a challenge in clinical dentistry. This study aimed to compare coronal discoloration induced by White Mineral Trioxide Aggregate and Calcium-enriched mixture cement. Fifty single-rooted, unrestored premolar teeth extracted for orthodontic reasons were selected. After access cavity preparation, all the root canals were instrumented with MTWO rotary files up to #40.6%. The specimens were randomly assigned to two experimental groups, White Mineral Trioxide Aggregate and Calcium-enriched mixture cement groups (n = 20), and two control groups (n = 5). In the White Mineral Trioxide Aggregate and Calcium-enriched mixture cement groups, the material was condensed via the access cavity 3 mm below the cementoenamel junction to a thickness of 3 mm. Tooth color was assessed using computer analysis of digital images. Tooth color measurements were recorded at eight time intervals: before material placement (but after tooth preparation), at 24 h, 48 h, one week, two weeks, four weeks, eight weeks, and sixteen weeks after material placement. Data were analyzed using t-test, ANOVA, repeated measure ANOVA, and Tukey HSD tests. The significance level was set at 5% for all the tests. Cervical discoloration of teeth in both experimental groups significantly increased over time (p < 0.05). However, samples in the White Mineral Trioxide Aggregate group showed more discoloration in cervical regions than Calcium-enriched mixture cement specimens after two, four, eight, and sixteen weeks (p < 0.05). Applying both White Mineral Trioxide Aggregate and Calcium-enriched mixture cement induced coronal discoloration; however, White Mineral Trioxide Aggregate samples exhibited greater cervical discoloration than Calcium-enriched mixture cement specimens after two, four, eight, and sixteen weeks.