We present a detailed investigation of the changes in the local structure and chemical disorder induced by controlled potential cycling in Pt3±d Co nanoparticles used as a catalyst in the Proton Exchange Membrane Fuel Cell (PEMFC) technology. Various state-of-the art material science techniques were used to study the microscopic properties of those nanomaterials including: ex-situ and in-situ X-ray Absorption Spectroscopy (XAS), X-Ray Diffraction (XRD), and Transmission Electron Microscopy (TEM). XAS double-edge multiple-scattering structural refinements of the Pt-Co spectra were performed taking into account the reduction of coordination numbers and degeneracy of three-atom configurations resulting from the measured size distribution obtained by TEM and XRD. The effect of chemical disorder in the considered nanoalloy was also taken into consideration. The PEMFC performance appears to be related to specific changes of the microscopic structural properties of the nanocatalyst during the first operation hours, especially during a cell activation period. In operating PEMFCs a small amount of Co oxide, initially present in the nanoalloy (on the surface of particles), disappeared gradually. At the same time, interatomic Pt-Pt and Pt-Co distances were slightly longer for higher current densities, while distance variances (s 2) tended to decrease. Co-Co distribution remained unchanged. By combining XRD and XAS data, we also found that after controlled potential cycling in PEMFC the stoichiometry of the considered alloy changed from the initial Pt3±d Co to Pt4±dCo. The comparison of XAS and XRD-extracted values of the Co atomic fraction indicated that mainly cobalt not fully alloyed with platinum dissolved and this process occured in the first degradation period. At the same time, no substantial aggregation processes and no change in the mean size of nanoparticles, were observed for this alloy. Accelerated degradation test, lasting up to 150 h, showed structural and electrochemical catalyst stability. Observed increase of chemical and local structural order of particle core alloy did not affect the ORR kinetics. Keywords: Structure, Nanoalloy, XAFS, Catalyst Degradation

Local Ordering Changes in Pt-Co Nanocatalyst Induced by Fuel Cell Working Conditions / Greco, G; Witkowska, ; Agnieszka, ; Minicucci, ; Marco, ; Olivi, ; Luca, ; Principi, ; Emiliano, ; Dsoke, ; Sonia, ; Moretti, ; Arianna, ; Marassi, ; Di, Cicco; Andrea,. - In: JOURNAL OF PHYSICAL CHEMISTRY. C.. - ISSN 1932-7455. - jp-2011-099569.R2(2012), pp. 12791-12802. [dx.doi.org/10.1021/jp2099569]

Local Ordering Changes in Pt-Co Nanocatalyst Induced by Fuel Cell Working Conditions

Greco G;
2012

Abstract

We present a detailed investigation of the changes in the local structure and chemical disorder induced by controlled potential cycling in Pt3±d Co nanoparticles used as a catalyst in the Proton Exchange Membrane Fuel Cell (PEMFC) technology. Various state-of-the art material science techniques were used to study the microscopic properties of those nanomaterials including: ex-situ and in-situ X-ray Absorption Spectroscopy (XAS), X-Ray Diffraction (XRD), and Transmission Electron Microscopy (TEM). XAS double-edge multiple-scattering structural refinements of the Pt-Co spectra were performed taking into account the reduction of coordination numbers and degeneracy of three-atom configurations resulting from the measured size distribution obtained by TEM and XRD. The effect of chemical disorder in the considered nanoalloy was also taken into consideration. The PEMFC performance appears to be related to specific changes of the microscopic structural properties of the nanocatalyst during the first operation hours, especially during a cell activation period. In operating PEMFCs a small amount of Co oxide, initially present in the nanoalloy (on the surface of particles), disappeared gradually. At the same time, interatomic Pt-Pt and Pt-Co distances were slightly longer for higher current densities, while distance variances (s 2) tended to decrease. Co-Co distribution remained unchanged. By combining XRD and XAS data, we also found that after controlled potential cycling in PEMFC the stoichiometry of the considered alloy changed from the initial Pt3±d Co to Pt4±dCo. The comparison of XAS and XRD-extracted values of the Co atomic fraction indicated that mainly cobalt not fully alloyed with platinum dissolved and this process occured in the first degradation period. At the same time, no substantial aggregation processes and no change in the mean size of nanoparticles, were observed for this alloy. Accelerated degradation test, lasting up to 150 h, showed structural and electrochemical catalyst stability. Observed increase of chemical and local structural order of particle core alloy did not affect the ORR kinetics. Keywords: Structure, Nanoalloy, XAFS, Catalyst Degradation
2012
01 Pubblicazione su rivista::01a Articolo in rivista
Local Ordering Changes in Pt-Co Nanocatalyst Induced by Fuel Cell Working Conditions / Greco, G; Witkowska, ; Agnieszka, ; Minicucci, ; Marco, ; Olivi, ; Luca, ; Principi, ; Emiliano, ; Dsoke, ; Sonia, ; Moretti, ; Arianna, ; Marassi, ; Di, Cicco; Andrea,. - In: JOURNAL OF PHYSICAL CHEMISTRY. C.. - ISSN 1932-7455. - jp-2011-099569.R2(2012), pp. 12791-12802. [dx.doi.org/10.1021/jp2099569]
File allegati a questo prodotto
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11573/1555175
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 24
  • ???jsp.display-item.citation.isi??? 21
social impact