The adsorption of diclofenac on thermo-plasma expanded graphite (a commercial product) from water solutions was investigated. The adsorbent material was characterized by SEM, TEM, BET, Raman and X-ray diffraction analyses. Typical diffractogram and Raman spectrum of graphitic material, dimension of 24.02 nm as crystallite dimension and a surface area of 47 m2 g−1 were obtained. The effect of pH on the adsorption capacity was evaluated in the range 1–7 and the adsorption mechanism was described by kinetic and isothermal studies. Pseudo-second order and Dubinin–Radushkevich models agreed with theoretical values of adsorption capacity (i.e. 400 and 433 mg g−1, respectively) and resulted to be the best fit for kinetics and isothermal experimental data. The thermodynamics of the process was evaluated by plotting the adsorption capacity/concentration ratio at the equilibrium as a function of different values of the multiplicative inverse of temperature. Moreover, the adsorbent regeneration was also investigated, comparing two different remediation techniques. Solvent washing performed with NaOH 0.2 M and thermo-treatment carried out by heating in an oven at 105 °C for 2 h and then at 200 °C for 4 h. The thermo-treatment was the best technique to regenerate the adsorbent, ensuring same performance after 4 cycles of use and regeneration.
Removal of diclofenac from aqueous solutions by adsorption on thermo-plasma expanded graphite / Cuccarese, M.; Brutti, S.; De Bonis, A.; Teghil, R.; Mancini, I. M.; Masi, S.; Caniani, D.. - In: SCIENTIFIC REPORTS. - ISSN 2045-2322. - 11:1(2021), pp. 1-15. [10.1038/s41598-021-83117-z]
Removal of diclofenac from aqueous solutions by adsorption on thermo-plasma expanded graphite
Brutti S.;
2021
Abstract
The adsorption of diclofenac on thermo-plasma expanded graphite (a commercial product) from water solutions was investigated. The adsorbent material was characterized by SEM, TEM, BET, Raman and X-ray diffraction analyses. Typical diffractogram and Raman spectrum of graphitic material, dimension of 24.02 nm as crystallite dimension and a surface area of 47 m2 g−1 were obtained. The effect of pH on the adsorption capacity was evaluated in the range 1–7 and the adsorption mechanism was described by kinetic and isothermal studies. Pseudo-second order and Dubinin–Radushkevich models agreed with theoretical values of adsorption capacity (i.e. 400 and 433 mg g−1, respectively) and resulted to be the best fit for kinetics and isothermal experimental data. The thermodynamics of the process was evaluated by plotting the adsorption capacity/concentration ratio at the equilibrium as a function of different values of the multiplicative inverse of temperature. Moreover, the adsorbent regeneration was also investigated, comparing two different remediation techniques. Solvent washing performed with NaOH 0.2 M and thermo-treatment carried out by heating in an oven at 105 °C for 2 h and then at 200 °C for 4 h. The thermo-treatment was the best technique to regenerate the adsorbent, ensuring same performance after 4 cycles of use and regeneration.File | Dimensione | Formato | |
---|---|---|---|
Cuccarese_Removal_2021.pdf
accesso aperto
Tipologia:
Versione editoriale (versione pubblicata con il layout dell'editore)
Licenza:
Creative commons
Dimensione
1.52 MB
Formato
Adobe PDF
|
1.52 MB | Adobe PDF |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.