Degradation of post-consumer PLA. Hydrolysis of polymeric matrix and oligomers stabilization in aqueous phase

Degradation of post-consumer PLA to lactic acid was analysed in order to assess the economic feasibility of the PLA chemical recycling process. Hydrolysis of PLA, in batch reactor, was analysed in the temperature range of 443-473K, under autogenous pressure and a constant PLA to water ratio (equal to approximately 0.11 by weight), without the use of a catalyst. The experimental results suggest that the complete degradation of PLA can be obtained using relatively low reaction-times with the production of a mixture containing the monomer and traces of the dimer of lactic acid. The overall process was modelled using a two-step process: bulk degradation of PLA (in the solid or molten phase) with the solubilisation of low molecular weight oligomers, and their subsequent hydrolysis in water (stabilization). The model describes the trend of oligomer concentrations in the aqueous phase and PLA conversion as a function of time with both high accuracy and agreement with experimental results.