This study focuses on Ni substitution in Y-Ba-Cu-O. Tc is decreasing monotonically up to 7% Ni doping but it reproducibly increases (84 K) for the 10% sample. Both orthorhombicity (b-a) and ``c'', and also the oxygen content do not decrease continuously as Ni concentration is increased.

Superconductivity in Ni Doped 123 Compound / K. B., Garg; Saini, Naurang Lal; P., Srivastava; R. K., Sharma; K. V. R., Rao; B. R. SEKHAR AND G. L., Dwivedi. - In: PHYSICA. B, CONDENSED MATTER. - ISSN 0921-4526. - STAMPA. - 163(1990), p. 249. [10.1016/0921-4526(90)90182-T]

Superconductivity in Ni Doped 123 Compound

SAINI, Naurang Lal;
1990

Abstract

This study focuses on Ni substitution in Y-Ba-Cu-O. Tc is decreasing monotonically up to 7% Ni doping but it reproducibly increases (84 K) for the 10% sample. Both orthorhombicity (b-a) and ``c'', and also the oxygen content do not decrease continuously as Ni concentration is increased.
File allegati a questo prodotto
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/11573/131987
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 0
  • ???jsp.display-item.citation.isi??? 1
social impact