Carbon nano/micro-structures used as fillers in metallic lightweight alloys matrix composites are receiving considerable attention in scientific research and industrial applications. Aluminum and magnesium are the most studied light metals used as matrices in metal composites materials principally for their low density (respectively 2.7 g/cm3 and 1.7 g/cm3) and low melting temperature (around 660 °C for both metals). A good interaction between matrix and fillers is the first step to obtain an increase in bulk properties; furthermore, the manufacturing procedure of the composite is fundamental in terms of quality of fillers dispersion. In this work the influence of surface modifications for three classes of carbon fillers for aluminum and magnesium alloy (AZ63) as matrices is studied. In particular, the selected fillers are short carbon micro fibres (SCMFs), carbon woven fabrics (CWF) and unidirectional yarn carbon fibres (UYFs). The surface modification was carried out by a direct coating of pure nickel on fibres. The electroless pure nickel plating was chosen as coating technique and the use of hydrazine as reducing agent has prevented the co-deposition of other elements (such as P or B). SEM and EDS analyses were performed to study the effect of surface modifications. The mechanical properties of manufactured composites were evaluated by four point flexural tests according to ASTM C1161 (room temperature). Results confirm improved interactions between matrix and fillers, and the specific interaction was studied for any chosen reinforcement.
Lightweight metallic matrix composites. Development of new composites material reinforced with carbon structures / Valente, Marco; Marini, Danilo; Genova, Virgilio; Quitadamo, Alessia; Marra, Francesco; Pulci, Giovanni. - In: JOURNAL OF APPLIED BIOMATERIALS & FUNCTIONAL MATERIALS. - ISSN 2280-8000. - 17:1 suppl(2019). [10.1177/2280800019840294]
Lightweight metallic matrix composites. Development of new composites material reinforced with carbon structures
Marco Valente
Writing – Review & Editing
;Danilo MariniWriting – Original Draft Preparation
;Virgilio GenovaValidation
;Alessia QuitadamoWriting – Review & Editing
;Francesco MarraData Curation
;Giovanni PulciData Curation
2019
Abstract
Carbon nano/micro-structures used as fillers in metallic lightweight alloys matrix composites are receiving considerable attention in scientific research and industrial applications. Aluminum and magnesium are the most studied light metals used as matrices in metal composites materials principally for their low density (respectively 2.7 g/cm3 and 1.7 g/cm3) and low melting temperature (around 660 °C for both metals). A good interaction between matrix and fillers is the first step to obtain an increase in bulk properties; furthermore, the manufacturing procedure of the composite is fundamental in terms of quality of fillers dispersion. In this work the influence of surface modifications for three classes of carbon fillers for aluminum and magnesium alloy (AZ63) as matrices is studied. In particular, the selected fillers are short carbon micro fibres (SCMFs), carbon woven fabrics (CWF) and unidirectional yarn carbon fibres (UYFs). The surface modification was carried out by a direct coating of pure nickel on fibres. The electroless pure nickel plating was chosen as coating technique and the use of hydrazine as reducing agent has prevented the co-deposition of other elements (such as P or B). SEM and EDS analyses were performed to study the effect of surface modifications. The mechanical properties of manufactured composites were evaluated by four point flexural tests according to ASTM C1161 (room temperature). Results confirm improved interactions between matrix and fillers, and the specific interaction was studied for any chosen reinforcement.File | Dimensione | Formato | |
---|---|---|---|
Valente_Lightweight-metallic_2019.pdf
accesso aperto
Tipologia:
Versione editoriale (versione pubblicata con il layout dell'editore)
Licenza:
Creative commons
Dimensione
1.58 MB
Formato
Adobe PDF
|
1.58 MB | Adobe PDF |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.