Double-nanotextured black diamond films with different geometries were fabricated by double-step femtosecond laser treatments at different split ratios of accumulated laser fluence. A “2D-like” pseudo-periodic nanostructure was obtained for the first time when the split ratio was slightly unbalanced in favour of the first step of the treatment, as inferred by scanning electron microscopy. Raman analysis showed that a residual biaxial stress, composed by a superposition of a tensile and a compressive component, is always present after the laser writing process, and that the two components tend to balance each other in the 2D pseudo-periodic case. Spectrophotometric measurements in the 200–2000 nm wavelength range returned outstanding solar absorptance values for all the fabricated films (reaching the unprecedented value of 99.1% in the “2D-like” structure), launching double-nanotextured black diamond as a possible alternative to black silicon as absorbing layer for high-efficiency solar cells.

Optical characterization of double-nanotextured black diamond films / Girolami, M.; Bellucci, A.; Mastellone, M.; Orlando, S.; Valentini, V.; Montereali, R. M.; Vincenti, M. A.; Polini, R.; Trucchi, D. M.. - In: CARBON. - ISSN 0008-6223. - 138:(2018), pp. 384-389. [10.1016/j.carbon.2018.07.055]

Optical characterization of double-nanotextured black diamond films

Mastellone, M.;
2018

Abstract

Double-nanotextured black diamond films with different geometries were fabricated by double-step femtosecond laser treatments at different split ratios of accumulated laser fluence. A “2D-like” pseudo-periodic nanostructure was obtained for the first time when the split ratio was slightly unbalanced in favour of the first step of the treatment, as inferred by scanning electron microscopy. Raman analysis showed that a residual biaxial stress, composed by a superposition of a tensile and a compressive component, is always present after the laser writing process, and that the two components tend to balance each other in the 2D pseudo-periodic case. Spectrophotometric measurements in the 200–2000 nm wavelength range returned outstanding solar absorptance values for all the fabricated films (reaching the unprecedented value of 99.1% in the “2D-like” structure), launching double-nanotextured black diamond as a possible alternative to black silicon as absorbing layer for high-efficiency solar cells.
Chemistry (all)
01 Pubblicazione su rivista::01a Articolo in rivista
Optical characterization of double-nanotextured black diamond films / Girolami, M.; Bellucci, A.; Mastellone, M.; Orlando, S.; Valentini, V.; Montereali, R. M.; Vincenti, M. A.; Polini, R.; Trucchi, D. M.. - In: CARBON. - ISSN 0008-6223. - 138:(2018), pp. 384-389. [10.1016/j.carbon.2018.07.055]
File allegati a questo prodotto
File Dimensione Formato  
1-s2.0-S000862231830705X-main.pdf

solo gestori archivio

Tipologia: Versione editoriale (versione pubblicata con il layout dell'editore)
Licenza: Tutti i diritti riservati (All rights reserved)
Dimensione 1.54 MB
Formato Adobe PDF
1.54 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11573/1179139
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 22
  • ???jsp.display-item.citation.isi??? 22
social impact