The effect of cycles of sterilization procedures on nickel-titanium (NiTi) endodontic instruments is a serious concern for practitioners. There is no agreement in the literature whether these procedures could adversely affect the mechanical properties of endodontic files, and, consequently, increase the risk of intracanal failure. The purpose of this study was to evaluate the mechanichal resistance of Hero (MicroMega, Besancon, France) instruments, before and after sterilization procedures. Thirty 02, 04, 06 tapered Hero size 30 new instruments were chosen and divided into 3 groups. Group A (control) were tested according to ANSI/ADA Spec.no 28 for torsional resistance, angle of torque and angle at breakage (45 inverted exclamation mark ). Group B files were first sterilized with chemiclave for 10 cycles of 20 minutes at 124 inverted exclamation mark C and then tested as described above. Group C files were first sterilized with glass beads for 10 cycles of 20 sec. at 250 inverted exclamation mark C and then tested as described above. Data were collected and statistically analyzed (t-paired test). Differences among the 3 groups were statistically not significant for both tests. All data were well within Spec.no 28 standard values. From the results of the present study, we may conclude that repeated sterilization procedures do not adversely affect the mechanichal resistance of Hero files.

[Mechanical properties of nickel-titanium files following multiple heat sterilizations] / Testarelli, Luca; Gallottini, Livio; Gambarini, Gianluca. - In: MINERVA STOMATOLOGICA. - ISSN 0026-4970. - 52:4(2003), pp. 169-173.

[Mechanical properties of nickel-titanium files following multiple heat sterilizations].

TESTARELLI, Luca;GALLOTTINI, Livio;GAMBARINI, Gianluca
2003

Abstract

The effect of cycles of sterilization procedures on nickel-titanium (NiTi) endodontic instruments is a serious concern for practitioners. There is no agreement in the literature whether these procedures could adversely affect the mechanical properties of endodontic files, and, consequently, increase the risk of intracanal failure. The purpose of this study was to evaluate the mechanichal resistance of Hero (MicroMega, Besancon, France) instruments, before and after sterilization procedures. Thirty 02, 04, 06 tapered Hero size 30 new instruments were chosen and divided into 3 groups. Group A (control) were tested according to ANSI/ADA Spec.no 28 for torsional resistance, angle of torque and angle at breakage (45 inverted exclamation mark ). Group B files were first sterilized with chemiclave for 10 cycles of 20 minutes at 124 inverted exclamation mark C and then tested as described above. Group C files were first sterilized with glass beads for 10 cycles of 20 sec. at 250 inverted exclamation mark C and then tested as described above. Data were collected and statistically analyzed (t-paired test). Differences among the 3 groups were statistically not significant for both tests. All data were well within Spec.no 28 standard values. From the results of the present study, we may conclude that repeated sterilization procedures do not adversely affect the mechanichal resistance of Hero files.
2003
01 Pubblicazione su rivista::01a Articolo in rivista
[Mechanical properties of nickel-titanium files following multiple heat sterilizations] / Testarelli, Luca; Gallottini, Livio; Gambarini, Gianluca. - In: MINERVA STOMATOLOGICA. - ISSN 0026-4970. - 52:4(2003), pp. 169-173.
File allegati a questo prodotto
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11573/253771
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? 2
  • Scopus 7
  • ???jsp.display-item.citation.isi??? ND
social impact