AIM: The aim of the present study was to investigate the in vitro sealing ability of a new obturating material (Real Seal 1, SybronEndo, Orange, CA, USA) and compare it with the Thermafil (Dentsply Maillefer, Baillargues, Switzerland) and One-Step systems (CMS Dental, Copenhagen, Denmark). METHODS: Forty-four freshly extracted lower premolars teeth were selected and a root canal treatment was performed using a crown-down Nickel-Titanium rotary preparation technique. Teeth were randomized into three groups (N.=14): 1) Thermafil group; 2) One/step group; 3) Real Seal 1 (RS1) group. The remaining two teeth served as controls. A fluid filtration system device was utilized to assess quantitatively the microleakage. Statistical analyses were performed by ANOVA and significance was set at 95%. RESULTS: Data clearly showed that the RS1 provided the best results, showing a minimal leakage after 24 hours. Statystical analysis showed a significant difference about the RS1 group, the Thermafil and One/Step group, while no significant differences were noted between these last two groups. Results show that the number of teeth that had no (=0) leakage was higher in the RS1 group (8 specimens) than in the remaining ones (1 and 1 specimen, respectively). CONCLUSIONS: Under the conditions of the present experimental test, the new RS1 material (carrier-based Resilon) provided excellent preliminary results showing sealing ability at 24 hours significantly better that traditional carrier-based gutta-percha systems.

Sealing ability of a new carrier-based obturating material / Testarelli, Luca; V., Milana; F., Rizzo; M., Gagliani; Gambarini, Gianluca. - In: MINERVA STOMATOLOGICA. - ISSN 0026-4970. - 58:5(2009), pp. 217-224.

Sealing ability of a new carrier-based obturating material.

TESTARELLI, Luca;GAMBARINI, Gianluca
2009

Abstract

AIM: The aim of the present study was to investigate the in vitro sealing ability of a new obturating material (Real Seal 1, SybronEndo, Orange, CA, USA) and compare it with the Thermafil (Dentsply Maillefer, Baillargues, Switzerland) and One-Step systems (CMS Dental, Copenhagen, Denmark). METHODS: Forty-four freshly extracted lower premolars teeth were selected and a root canal treatment was performed using a crown-down Nickel-Titanium rotary preparation technique. Teeth were randomized into three groups (N.=14): 1) Thermafil group; 2) One/step group; 3) Real Seal 1 (RS1) group. The remaining two teeth served as controls. A fluid filtration system device was utilized to assess quantitatively the microleakage. Statistical analyses were performed by ANOVA and significance was set at 95%. RESULTS: Data clearly showed that the RS1 provided the best results, showing a minimal leakage after 24 hours. Statystical analysis showed a significant difference about the RS1 group, the Thermafil and One/Step group, while no significant differences were noted between these last two groups. Results show that the number of teeth that had no (=0) leakage was higher in the RS1 group (8 specimens) than in the remaining ones (1 and 1 specimen, respectively). CONCLUSIONS: Under the conditions of the present experimental test, the new RS1 material (carrier-based Resilon) provided excellent preliminary results showing sealing ability at 24 hours significantly better that traditional carrier-based gutta-percha systems.
2009
01 Pubblicazione su rivista::01a Articolo in rivista
Sealing ability of a new carrier-based obturating material / Testarelli, Luca; V., Milana; F., Rizzo; M., Gagliani; Gambarini, Gianluca. - In: MINERVA STOMATOLOGICA. - ISSN 0026-4970. - 58:5(2009), pp. 217-224.
File allegati a questo prodotto
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11573/229878
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? 2
  • Scopus 4
  • ???jsp.display-item.citation.isi??? ND
social impact