In the energy transition from fossil to clean fuels, hydrogen plays a key role. Proton-exchange membrane fuel cells (PEMFCs) represent the most promising hydrogen application, but they require a pure hydrogen stream (CO < 10 ppm). The steam iron process represents a technology for the production of pure H2, exploiting iron redox cycles. If renewable reducing agents are used, the process can be considered completely green. In this context, bio-ethanol can be an interesting solution that is still not thoroughly explored. In this work, the use of ethanol as a reducing agent in the steam iron process will be investigated. Ethanol, at high temperature, decomposes mainly in syngas but can also form coke, which can compromise the process effectiveness, reacting with water and producing CO together with H2. In this work, the deposition of coke is avoided by controlling the duration of the reduction step; in fact, the data demonstrated that coke deposition is significantly dependent on reduction time. Tests were carried out in a fixed bed reactor using hematite (Fe2O3) as raw iron oxide adopting several reduction times (7 minutes-25 minutes), which correspond to different amount of ethanol fed (5 mmolC2H5OH/gFe2O3-17,95 mmolC2H5OH/gFe2O3). The effect of the addition of MnO2 to increase the reduction degree of iron oxides was explored using different amount of MnO2 (10 wt% and 40 wt% with respect to Fe2O3). The tests were performed at fixed temperatures of 675°C and atmospheric pressure. The optimization of the reduction time, in the chosen operating condition, performed only with Fe2O3, shows that, feeding an amount of 5 mmolC2H5OH/gFe2O3, coke deposition is avoided and, therefore, a pure H2 stream in oxidation is obtained. The addition of MnO2 leads to increased H2 yield and process efficiency, confirming its positive effect on the reduction degree of the solid bed. A reaction pathway to demonstrate the synergic effect of Fe2O3 and MnO2 in the reduction step was proposed in this article.

Pure hydrogen production by steam-iron process. The synergic effect of MnO2 and Fe2O3 / De Filippis, P.; D'Alvia, L.; Damizia, M.; de Caprariis, B.; Del Prete, Z.. - In: INTERNATIONAL JOURNAL OF ENERGY RESEARCH. - ISSN 0363-907X. - 45:3(2021), pp. 4479-4494. [10.1002/er.6117]

Pure hydrogen production by steam-iron process. The synergic effect of MnO2 and Fe2O3

De Filippis P.;D'Alvia L.;Damizia M.
;
de Caprariis B.;Del Prete Z.
Ultimo
2021

Abstract

In the energy transition from fossil to clean fuels, hydrogen plays a key role. Proton-exchange membrane fuel cells (PEMFCs) represent the most promising hydrogen application, but they require a pure hydrogen stream (CO < 10 ppm). The steam iron process represents a technology for the production of pure H2, exploiting iron redox cycles. If renewable reducing agents are used, the process can be considered completely green. In this context, bio-ethanol can be an interesting solution that is still not thoroughly explored. In this work, the use of ethanol as a reducing agent in the steam iron process will be investigated. Ethanol, at high temperature, decomposes mainly in syngas but can also form coke, which can compromise the process effectiveness, reacting with water and producing CO together with H2. In this work, the deposition of coke is avoided by controlling the duration of the reduction step; in fact, the data demonstrated that coke deposition is significantly dependent on reduction time. Tests were carried out in a fixed bed reactor using hematite (Fe2O3) as raw iron oxide adopting several reduction times (7 minutes-25 minutes), which correspond to different amount of ethanol fed (5 mmolC2H5OH/gFe2O3-17,95 mmolC2H5OH/gFe2O3). The effect of the addition of MnO2 to increase the reduction degree of iron oxides was explored using different amount of MnO2 (10 wt% and 40 wt% with respect to Fe2O3). The tests were performed at fixed temperatures of 675°C and atmospheric pressure. The optimization of the reduction time, in the chosen operating condition, performed only with Fe2O3, shows that, feeding an amount of 5 mmolC2H5OH/gFe2O3, coke deposition is avoided and, therefore, a pure H2 stream in oxidation is obtained. The addition of MnO2 leads to increased H2 yield and process efficiency, confirming its positive effect on the reduction degree of the solid bed. A reaction pathway to demonstrate the synergic effect of Fe2O3 and MnO2 in the reduction step was proposed in this article.
2021
bioethanol; chemical looping; efficiency measurement; hydrogen; manganese oxides; steam-iron process
01 Pubblicazione su rivista::01a Articolo in rivista
Pure hydrogen production by steam-iron process. The synergic effect of MnO2 and Fe2O3 / De Filippis, P.; D'Alvia, L.; Damizia, M.; de Caprariis, B.; Del Prete, Z.. - In: INTERNATIONAL JOURNAL OF ENERGY RESEARCH. - ISSN 0363-907X. - 45:3(2021), pp. 4479-4494. [10.1002/er.6117]
File allegati a questo prodotto
File Dimensione Formato  
De-Filippis_Pure-hydrogen-production_postprint_2021.pdf

Open Access dal 25/11/2021

Note: https://onlinelibrary.wiley.com/doi/epdf/10.1002/er.6117
Tipologia: Documento in Post-print (versione successiva alla peer review e accettata per la pubblicazione)
Licenza: Altra licenza (allegare)
Dimensione 953.97 kB
Formato Adobe PDF
953.97 kB Adobe PDF
De-Filippis_Pure-hydrogen-production_licenza_2020.pdf

solo gestori archivio

Note: early printer
Tipologia: Licenza (contratto editoriale)
Licenza: Tutti i diritti riservati (All rights reserved)
Dimensione 15.46 kB
Formato Adobe PDF
15.46 kB Adobe PDF   Contatta l'autore

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11573/1449669
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 15
  • ???jsp.display-item.citation.isi??? 9
social impact